PLASMA SPRAY WELDING POWER |
|||||||||||||||||||
| Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Hardness Of Deposited Metal | Application | ||||||||||||
| C | S | P | Si | Mn | Cr | B | Mo | Fe | Others | ||||||||||
| SS.F321 | - | - | - | - | 0.059 | 0.009 | 0.026 | 1.75 | 0.35 | 17.28 | 1.41 | 0.23 | Rem | - | HRC:39 | Ferro-based Cr13 type is suitable for axles and valves of carbon steel or alloy steel whose working temperature is lower than 450℃, and its performance is better than D507 electrode. | |||
| SS.F321T | - | - | - | - | 0.12 | 0.009 | 0.025 | 1.61 | 0.29 | 16.81 | 1.53 | 0.39 | Rem | - | HRC:47 | Ferro-based chromium-nickel-molybdenum type, suitable for cladding 316 forgings. | |||
| SS.F321H | - | - | - | - | 0.12 | - | - | 1.20 | - | 13.40 | 1.43 | 0.80 | Rem | - | HRC:50 | Iron-based Cr13 is suitable for axles and valves of carbon steel or alloy steel whose surfacing temperature is lower than 450 C. It has higher hardness than F321. | |||
| SS.F322 | - | - | - | - | 0.098 | 0.007 | 0.025 | 1.80 | - | 20.52 | 1.53 | 2.83 | Rem | Ni:11.85 | HRC:28 | Ferro-based chromium-nickel-silicon type is suitable for valve sealing surface and other sealing parts of high-pressure boiler device in power plant whose working temperature is below 570℃, and its performance is superior to D547 electrode. | |||
| SS.F327 | - | - | - | - | 0.085 | 0.009 | 0.030 | 2.97 | 0.76 | 20.81 | 1.67 | 0.25 | Rem | Ni:11.30 | HRC:34 | Ferro-based chromium-nickel-silicon type is suitable for valve sealing surface and other sealing parts of high-pressure boiler device in power plant whose working temperature is lower than 600℃. Its performance is superior to D547Mo electrode. | |||
| SS.F328 | - | - | - | - | 0.092 | 0.008 | 0.029 | 2.84 | - | 18.42 | 1.54 | 1.40 | Rem | Ni:9.25 W:1.21 |
HRC:39 | For caldding high-pressure valve sealing surface whose working temperature is below 600℃. | |||
| SS.F802 | - | - | - | - | 0.91 | - | - | 0.90 | 0.88 | 30.90 | - | - | 4.36 | Co:余量 W:5.20 |
HRC:42 | Used for caldding high temperature and high pressure valves, thermal cutting blade engine valves, etc. | |||
PLASMA SPRAY WELDING POWER |
|||||||||||||||||||
| Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Hardness Of Deposited Metal | Application | ||||||||||||
| C | S | P | Si | Mn | Cr | B | Mo | Fe | Others | ||||||||||
| SS.F321 | - | - | - | - | 0.059 | 0.009 | 0.026 | 1.75 | 0.35 | 17.28 | 1.41 | 0.23 | Rem | - | HRC:39 | Ferro-based Cr13 type is suitable for axles and valves of carbon steel or alloy steel whose working temperature is lower than 450℃, and its performance is better than D507 electrode. | |||
| SS.F321T | - | - | - | - | 0.12 | 0.009 | 0.025 | 1.61 | 0.29 | 16.81 | 1.53 | 0.39 | Rem | - | HRC:47 | Ferro-based chromium-nickel-molybdenum type, suitable for cladding 316 forgings. | |||
| SS.F321H | - | - | - | - | 0.12 | - | - | 1.20 | - | 13.40 | 1.43 | 0.80 | Rem | - | HRC:50 | Iron-based Cr13 is suitable for axles and valves of carbon steel or alloy steel whose surfacing temperature is lower than 450 C. It has higher hardness than F321. | |||
| SS.F322 | - | - | - | - | 0.098 | 0.007 | 0.025 | 1.80 | - | 20.52 | 1.53 | 2.83 | Rem | Ni:11.85 | HRC:28 | Ferro-based chromium-nickel-silicon type is suitable for valve sealing surface and other sealing parts of high-pressure boiler device in power plant whose working temperature is below 570℃, and its performance is superior to D547 electrode. | |||
| SS.F327 | - | - | - | - | 0.085 | 0.009 | 0.030 | 2.97 | 0.76 | 20.81 | 1.67 | 0.25 | Rem | Ni:11.30 | HRC:34 | Ferro-based chromium-nickel-silicon type is suitable for valve sealing surface and other sealing parts of high-pressure boiler device in power plant whose working temperature is lower than 600℃. Its performance is superior to D547Mo electrode. | |||
| SS.F328 | - | - | - | - | 0.092 | 0.008 | 0.029 | 2.84 | - | 18.42 | 1.54 | 1.40 | Rem | Ni:9.25 W:1.21 |
HRC:39 | For caldding high-pressure valve sealing surface whose working temperature is below 600℃. | |||
| SS.F802 | - | - | - | - | 0.91 | - | - | 0.90 | 0.88 | 30.90 | - | - | 4.36 | Co:余量 W:5.20 |
HRC:42 | Used for caldding high temperature and high pressure valves, thermal cutting blade engine valves, etc. | |||