STAINLESS STEEL SUBMERGED ARC WIRE AND FLUX |
|||||||||||||||||||
| Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Mechanical Properties Of Deposited Metal | Application | ||||||||||||
| C | Mn | Si | P | S | Cr | Ni | Others | Y.P.(Mpa) | T.S.(Mpa) | E.L.(%) | I.V.(J) | ||||||||
| WWS-308 WXS-601 | 2.5/3.2/4.0 | NB/T F308-H0Cr21Ni10 GB/T S F308L FB-S308L |
PA,PB,PC | DC+ | 0.040 | 1.77 | 0.37 | 0.021 | 0.008 | 20.28 | 9.28 | - | - | - | - | 585 | 41 | - | The chemical composition of 18%Cr-8%Ni is excellent in weldability. |
| WWS-308L WXS-601 | 2.5/3.2/4.0 | NB/T F308L-H00Cr21Ni10 GB/T S F308 FB-S308 |
PA,PB,PC | DC+ | 0.039 | 1.77 | 0.45 | 0.022 | 0.010 | 19.55 | 9.35 | - | - | - | - | 590 | 39 | - | The chemical composition of low-C 18%Cr-8%Ni is excellent in weldability. |
| WWS-309L WXS-601 | 2.5/3.2/4.0 | NB/T F309L-H022Cr24Ni13 GB/T S F309L FB-S309L |
PA,PB,PC | DC+ | 0.026 | 1.55 | 0.36 | 0.025 | 0.011 | 22.95 | 12.51 | - | - | - | - | 570 | 36 | - | Low C-22%Cr-12%Ni chemical composition, excellent weldability, suitable for stainless steel and carbon steel or low alloy steel welding. |
| WWS-316L WXS-601 | 2.5/3.2/4.0 | NB/T F316L-H00Cr19Ni12Mo2 GB/T S F316L FB-S316L |
PA,PB,PC | DC+ | 0.025 | 1.31 | 0.55 | 0.026 | 0.012 | 18.81 | 11.50 | Mo:2.03 | - | - | - | 555 | 40 | - | Low C-18%Cr-12%Ni-2%Mo chemical composition, excellent weldability. |
| WWS-347 WXS-667 | 2.5/3.2/4.0 | NB/T F347-H06Cr21Ni10Nb GB/T S F347 FB-S347 |
PA,PB,PC | DC+ | 0.044 | 1.87 | 0.81 | 0.018 | 0.012 | 20.03 | 9.83 | Nb:0.42 | - | - | - | 555 | 36 | - | The chemical composition of 18%Cr-11%Ni-Nb is excellent in weldability and intergranular corrosion resistance. |
STAINLESS STEEL SUBMERGED ARC WIRE AND FLUX |
|||||||||||||||||||
| Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Mechanical Properties Of Deposited Metal | Application | ||||||||||||
| C | Mn | Si | P | S | Cr | Ni | Others | Y.P.(Mpa) | T.S.(Mpa) | E.L.(%) | I.V.(J) | ||||||||
| WWS-308 WXS-601 | 2.5/3.2/4.0 | NB/T F308-H0Cr21Ni10 GB/T S F308L FB-S308L |
PA,PB,PC | DC+ | 0.040 | 1.77 | 0.37 | 0.021 | 0.008 | 20.28 | 9.28 | - | - | - | - | 585 | 41 | - | The chemical composition of 18%Cr-8%Ni is excellent in weldability. |
| WWS-308L WXS-601 | 2.5/3.2/4.0 | NB/T F308L-H00Cr21Ni10 GB/T S F308 FB-S308 |
PA,PB,PC | DC+ | 0.039 | 1.77 | 0.45 | 0.022 | 0.010 | 19.55 | 9.35 | - | - | - | - | 590 | 39 | - | The chemical composition of low-C 18%Cr-8%Ni is excellent in weldability. |
| WWS-309L WXS-601 | 2.5/3.2/4.0 | NB/T F309L-H022Cr24Ni13 GB/T S F309L FB-S309L |
PA,PB,PC | DC+ | 0.026 | 1.55 | 0.36 | 0.025 | 0.011 | 22.95 | 12.51 | - | - | - | - | 570 | 36 | - | Low C-22%Cr-12%Ni chemical composition, excellent weldability, suitable for stainless steel and carbon steel or low alloy steel welding. |
| WWS-316L WXS-601 | 2.5/3.2/4.0 | NB/T F316L-H00Cr19Ni12Mo2 GB/T S F316L FB-S316L |
PA,PB,PC | DC+ | 0.025 | 1.31 | 0.55 | 0.026 | 0.012 | 18.81 | 11.50 | Mo:2.03 | - | - | - | 555 | 40 | - | Low C-18%Cr-12%Ni-2%Mo chemical composition, excellent weldability. |
| WWS-347 WXS-667 | 2.5/3.2/4.0 | NB/T F347-H06Cr21Ni10Nb GB/T S F347 FB-S347 |
PA,PB,PC | DC+ | 0.044 | 1.87 | 0.81 | 0.018 | 0.012 | 20.03 | 9.83 | Nb:0.42 | - | - | - | 555 | 36 | - | The chemical composition of 18%Cr-11%Ni-Nb is excellent in weldability and intergranular corrosion resistance. |